Electron-beam technology

In a vacuum, the electron beam provides a source of heat that can melt or modify any material.[2] This source of heat or phase transformation is absolutely sterile due to the vacuum and scull of solidified metal around the cold copper crucible walls. This ensures that the purest materials can be produced and refined in electron-beam vacuum furnaces. Rare and refractory metals can be produced or refined in small-volume vacuum furnaces. For mass production of steels, large furnaces with capacity measured in metric tons and electron-beam power in megawatts exist in industrialized countries.

Since the beginning of electron-beam welding on an industrial scale at the end of the 1950s, countless electron-beam welders have been designed and are being used worldwide. These welders feature working vacuum chambers ranging from a few liters up to hundreds of cubic meters, with electron guns carrying power of up to 100 kW.

Modern electron-beam welders are usually designed with a computer-controlled deflection system that can traverse the beam rapidly and accurately over a selected area of the work piece. Thanks to the rapid heating, only a thin surface layer of the material is heated. Applications include hardening, annealing, tempering, texturing, and polishing (with argon gas present). If the electron beam is used to cut a shallow trough in the surface, repeatedly moving it horizontally along the trough at high speeds creates a small pile of ejected melted metal. With repetition, spike structures of up to a millimeter in height can be created. These structures can aid bonding between different materials and modify the surface roughness of the metal.

Additive manufacturing is the process of joining materials to make objects from 3D model data, usually by melting powder material layer upon layer. Melting in a vacuum by using a computer-controlled scanning electron beam is highly precise. Electron-beam direct manufacturing (DM) is the first commercially available, large-scale, fully programmable means of achieving near net shape parts.

The source billet metal is melted by an electron beam while being spun vigorously. Powder is produced as the metal cools when flying off the metal bar.

Electron-beam machining is a process in which high-velocity electrons are concentrated into a narrow beam with a very high planar power density. The beam cross-section is then focused and directed toward the work piece, creating heat and vaporizing the material. Electron-beam machining can be used to accurately cut or bore a wide variety of metals. The resulting surface finish is better and kerf width is narrower than what can be produced by other thermal cutting processes. However, due to high equipment costs, the use of this technology is limited to high-value products.

An electron lithograph is produced by a very finely focused electron beam, which creates micro-structures in the resist that can subsequently be transferred to the substrate material, often by etching. It was originally developed for manufacturing integrated circuits and is also used for creating nanotechnology architectures. Electron lithographs uses electron beams with diameters ranging from two nanometers up to hundreds of nanometers. The electron lithograph is also used to produce computer-generated holograms (CGH). Maskless electron lithography has found wide usage in photomask making for photolithography, low-volume production of semiconductor components, and research and development activities.

Physical vapor deposition takes place in a vacuum and produces a thin film of solar cells by depositing thin layers of metals onto a backing structure. Electron-beam evaporation uses thermionics emission to create a stream of electrons that are accelerated by a high-voltage cathode and anode arrangement. Electrostatic and magnetic fields focus and direct the electrons to strike a target. The kinetic energy is transformed into thermal energy at or near the surface of the material. The resulting heating causes the material to melt and then evaporate. Temperatures in excess of 3500 degrees Celsius can be reached. The vapor from the source condenses onto a substrate, creating a thin film of high-purity material. Film thicknesses from a single atomic layer to many micrometers can be achieved. This technique is used in microelectronics, optics, and material research, and to produce solar cells and many other products.

Electron-beam curing is a method of curing paints and inks without the need for traditional solvent. Electron-beam curing produces a finish similar to that of traditional solvent-evaporation processes, but achieves that finish through a polymerization process.

An electron microscope uses a controlled beam of electrons to illuminate a specimen and produce a magnified image. Two common types are the scanning electron microscope (SEM) and the transmission electron microscope (TEM).

Electron beams impinging on metal produce X-rays. The X-rays may be diagnostic, e.g., dental or limb images. Often in these X-ray tubes the metal is a spinning disk so that it doesn't melt; the disk is spun in vacuum via a magnetic motor. The X-rays may also be used to kill cancerous tissue. The Therac25 machine is an infamous example of this.

Additive manufacturing is the process of joining materials to make objects fr